Materials | Specification | Requirements | |||
Standared | Mechanical Properties | ||||
Welded Pipe | Φ8×1.0×6000 _St12 |
OD | Φ8.0mm~8.10mm | T/S(Mpa) | ≥270MPa |
WT | 1.0±0.08 mm | E/S(Mpa) | (130-260)Mpa | ||
Height of ID Scarf | -0.05mm~+0.15mm | ||||
Expansion | >25% | expansion test | / | ||
Surface | GBK | crushing test | / | ||
Welded Pipe | Φ10×1.0×4500_St12 | OD | Φ10±0.1mm | T/S(Mpa) | ≥270MPa |
WT | 1.0±0.08 mm | E/S(Mpa) | (130-260)Mpa | ||
Height of ID Scarf | -0.05mm~+0.15mm | ||||
Expansion | >35% | expansion test | / | ||
Surface | GBK | crushing test | / | ||
Welded Pipe | Φ16×1.2×6000 _ST12 |
OD | Φ16±0.1mm | T/S(Mpa) | ≥270MPa |
WT | 1.2±0.1mm | E/S(Mpa) | (130-260)Mpa | ||
Height of ID Scarf | -0.05mm~+0.15mm | ||||
Expansion | >25% | expansion test | / | ||
Surface | GBK | crushing test | / | ||
Welded Pipe | Φ17.3×1.0×6000 _St12 |
OD | Φ17.3±0.1mm | T/S(Mpa) | ≥270MPa |
WT | 1.0±0.08 mm | E/S(Mpa) | (130-260)Mpa | ||
Height of ID Scarf | -0.05mm~+0.15mm | ||||
Expansion | >27% | expansion test | / | ||
Surface | GBK | crushing test | / | ||
Welded Pipe | Φ17.3×1.2×6000 _St12 |
OD | Φ17.3±0.1mm | T/S(Mpa) | ≥270MPa |
WT | 1.2±0.1mm | E/S(Mpa) | (130-260)Mpa | ||
Height of ID Scarf | -0.05mm~+0.15mm | ||||
Expansion | >28% | expansion test | / | ||
Surface | GBK | crushing test | / | ||
Welded Pipe | Φ28×1.2×6000 _ST12 |
OD | Φ28±0.1mm | T/S(Mpa) | ≥270MPa |
WT | 1.2±0.1mm | E/S(Mpa) | (130-260)Mpa | ||
Height of ID Scarf | -0.05mm~+0.15mm | ||||
Expansion | >15% | expansion test | / | ||
Surface | GBK | crushing test | / |